Online service
Hotline
0086-15255264774
  • Home   >   Products   >     >   Organic Polysilazane IOTA 9118
  • Organic Polysilazane IOTA 9118

      It is specially for high temperature resistance coating systems. MY 9118 has low viscosity and good adhesion, can be applied to various types of substrates by smearing, dipping, spraying, brushing and other methods, the main substrates are metals, alloys, glass, paint films and plastics (such as PP, PC, PVC, PMMA), etc.

       

      Product Features

      Low viscosity

      High temperature resistance

      Various curing methods

      Non-flammable after curing

      Anti-oxidation, anti-corrosion

      Easy to clean

      Good adhesion on the metal ceramic graphite materials

       

      Applications

      Coatings

      Adhesives

      Non-flammable composites

      Polymer matrix composites

      Glass and Abrasives

      Applications with low surface tension and easy to clean

       

      Technical index

      Appearance: light yellow transparent liquid

      Molecular weight (Mn): 1200-1400

      Solid content: ≥99% (other contents could be customized)

      Density: 0.98g/cm3-0.99g/cm3

      Ceramic density: 1.60-2.00 g/cm-3

      Viscosity: 10cp-40cp

      Cracking threshold: 100µm+(coating thickness)

      Cured hardness: 6-7H

      Hydrophobic angle: 100°-105°

      Recommended temperature of varnish coating: <800

      Recommended operating temperature with main coating: <1600

      Ceramic yield (800): 50%-60%

      Cured ceramic yield(800): 60%-70%

      Chemical masking: Well performed with O2H2O and other gas

      Linear shrinkage: <1%

      Transmittance (visible light): >95%

      Metal Adhesion (Cross-Hatch): 0 grade

      Shelf life: 12months in unopened condition

       

      Curing conditions

      1. High temperature curing

      a. without catalystHeating temperature250-350

      b. add Peroxide type thermal crosslinking agent③:Heating temperature120-180

      c. add platinum catalystHeating temperature: 80-100

      2. UV curing④:add Cleavage type photoinitiator

      The cured coating perform well in indoor environments, but the toughness of the coating will turn to be weak after 400.

       

      Notes

         The main functional group in MY 9118 is Vi, that will make the liquid to be light yellow, meanwhile the special additive in MY 9118 will get the same effect. But The cured coating will be colorless and transparent after the curing process(the additive will be released).

         MY 9118 will generate the coating film with no hardness, poor adhesion and transparency after 3 days cured in room temperature.

         MY 9118 could be cured with high temperature, it will reduce the heating temperature and curing time by adding the thermal crosslinking agentwhich has no effect on coating hardness, color, adhesion and other properties.

         The UV cured coating of MY 9118 perform well in room temperature, but the high temperature resistance is poor as cured by UV, the coating will turn to be yellowing when the temperature up to 300+.

         The operate temperature of MY 9118 coating is related to the film thickness. The higher thickness, the better protective performance, but it easy to crack in high temperature.

       

      Cracking conditions

      MY 9118 cured product converted to amorphous ceramics by high temperature cracking, eventually get crystalline ceramics. It is amorphous product below 1400 , begin to crystallize above 1400 . Ceramic product composition has great relationship with cracking atmosphere, SiC and Si3N4 under nitrogen or argon; mainly Si3N4 under Ammonia; mainly SiOCN under air conditions.

      In addition, the cured product cracking is easily influenced by filler, and result affects the composition of the final ceramic product.

       

      Compatibility

      The product could be miscible with most non-polar solvents, such as alkanes, ethers, ketones, esters. Insoluble in alcohol and ether solvents, such as diethylene glycol dimethyl ether, diethylene glycol dibutyl ether, tetraethyl ether Butyl glycol ether.

      It’s also miscible with a variety of resins, such as epoxy silicone resin, silicone resin, it will shorten the curing time and improve resin hardness when mixed with silicone resins.

       

      Operation Methods

      Operating and storing in a dry, cool and well-ventilated environment, away from heat and fire sources, the recommended temperature is 0-20.

      The gloves, masks, etc. is necessary when taking the product.

      Uncured product should not be placed close to fire sources, humid air, or water.

      The container must be replace the air with nitrogen/argon and completely sealed in time after use.

      Unused product that has been formulated cannot be recycled and should be disposed of in accordance with local regulations.

      Products beyond the shelf life can be used only after the retesting complied.

       

      Package

      Packed with metal container in 100ml, 1L and 5L.

       

      Clean

      Proper cleaning methods are important, quickly wipe down the surface with acetone or mineral spirits after use.

      Once MY 9118 is cured, the coating cannot be washed away by solvent.

       

      Precautions